Comparison of measured and modelled residual stresses in a welded P91 steel pipe undergoing post weld heat treatment

Research output: Contribution to journalArticlepeer-review

  • A. H. Yaghi
  • T. H. Hyde
  • Adib A. Becker
  • Wei Sun
  • Wu Wen
  • Gabrielle Hilson
  • Dr Sarinova Simandjuntak
  • Peter Flewitt
  • Martyn Pavier
  • David Smith
The process of fusion arc welding of steel pipes in power generation plants induces residual stresses which may be detrimental to the integrity and endurance of plant pipelines. P91 is high-grade steel used in the construction of pipelines carrying hot steam at high pressure, conditions which cause creep during service. Welded P91 pipes are usually subjected to post-weld heat treatment (PWHT) to mitigate the magnitude of residual stresses and temper the material, hence improving its resistance to creep. In this paper, the finite element (FE) method of modelling residual stresses due to PWHT in a circumferentially butt-welded P91 pipe is presented. The PWHT hold temperature is 760 ﰫC. The paper describes the X-Ray Diffraction (XRD) and Deep-Hole Drilling (DHD) experimental techniques and how they are applied to measure residual stresses in the welded P91 pipe after PWHT. The material property data, necessary for the FE simulation of PWHT, has been obtained from stress- relaxation tests on P91 uniaxial tensile specimens at 760 ﰫC. Good agreements have been achieved between the results of the FE method and the two sets of experimentally-measured residual stresses.
Original languageEnglish
Article number104076
Number of pages8
JournalInternational Journal of Pressure Vessels and Piping
Volume181
DOIs
Publication statusPublished - 19 Mar 2020

Documents

  • Comparison of measured and modelled residual stresses

    Accepted author manuscript (Post-print), 1.73 MB, PDF document

    Due to publisher’s copyright restrictions, this document is not freely available to download from this website until: 19/03/21

    Licence: CC BY-NC-ND

Related information

Relations Get citation (various referencing formats)

ID: 20199278